Density
|
1.32
|
--
|
g/cm³
|
ISO 1183
|
|
Molding Shrinkage
|
|
|
|
ISO 294-4
|
|
Across Flow
|
0.80
|
--
|
%
|
|
|
Flow
|
0.30
|
--
|
%
|
|
|
Water Absorption (24 hr)
|
0.83
|
--
|
%
|
ASTM D570
|
|
Viscosity Number
|
165
|
--
|
cm³/g
|
ISO 307
|
|
Tensile Modulus
|
1.26E+6
|
841000
|
psi
|
ISO 527-2
|
|
Tensile Stress (Break)
|
20600
|
13800
|
psi
|
ISO 527-2
|
|
Tensile Strain (Break)
|
4.0
|
5.0
|
%
|
ISO 527-2
|
|
Flexural Modulus
|
1.07E+6
|
754000
|
psi
|
ISO 178
|
|
Charpy Notched Impact Strength
|
|
|
|
ISO 179/1eA
|
|
-40°F
|
6.2
|
6.2
|
ft·lb/in²
|
|
|
-22°F
|
6.7
|
6.7
|
ft·lb/in²
|
|
|
73°F
|
9.5
|
10
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
|
ISO 179/1eU
|
|
-22°F
|
38
|
36
|
ft·lb/in²
|
|
|
73°F
|
43
|
38
|
ft·lb/in²
|
|
|
Notched Izod Impact Strength
|
|
|
|
ISO 180/1A
|
|
-40°F
|
7.1
|
4.8
|
ft·lb/in²
|
|
|
-22°F
|
6.7
|
4.8
|
ft·lb/in²
|
|
|
73°F
|
10
|
9.5
|
ft·lb/in²
|
|
|
Unnotched Izod Impact Strength
|
|
|
|
ISO 180/1U
|
|
-22°F
|
38
|
36
|
ft·lb/in²
|
|
|
73°F
|
35
|
38
|
ft·lb/in²
|
|
|
Heat Deflection Temperature
|
|
|
|
|
|
66 psi, Unannealed
|
504
|
--
|
°F
|
ISO 75-2/B
|
|
264 psi, Unannealed
|
477
|
--
|
°F
|
ISO 75-2/A
|
|
Melting Temperature 3
|
504
|
--
|
°F
|
ISO 11357-3
|
|
CLTE
|
|
|
|
ISO 11359-2
|
|
Flow
|
8.3E-6
|
--
|
in/in/°F
|
|
|
Transverse
|
6.6E-5
|
--
|
in/in/°F
|
|
|
Comparative Tracking Index
|
600
|
--
|
V
|
IEC 60112
|
|
Flammability Classification
|
|
|
|
IEC 60695-11-10, -20
|
|
0.0295 in
|
HB
|
--
|
|
|
|
0.0591 in
|
HB
|
--
|
|
|
|
Oxygen Index
|
23
|
--
|
%
|
ISO 4589-2
|
|
Melt Density
|
1.12
|
--
|
g/cm³
|
|
|
Specific Heat Capacity of Melt
|
0.526
|
--
|
Btu/lb/°F
|
|
|
Thermal Conductivity of Melt
|
1.5
|
--
|
Btu·in/hr/ft²/°F
|
|
|