比重
|
1.19
|
g/cm³
|
ASTM D792
|
|
特定体积
|
0.830
|
cm³/g
|
ASTM D792
|
|
熔流率（熔体流动速率）
|
|
|
ASTM D1238
|
|
300°C/1.2 kg
|
2.0
|
g/10 min
|
|
|
300°C/6.1 kg
|
9.0
|
g/10 min
|
|
|
收缩率 - 流动 (3.20 mm)
|
0.80 到 1.0
|
%
|
内部方法
|
|
吸水率 (24 hr)
|
0.19
|
%
|
ASTM D570
|
|
洛氏硬度
|
|
|
ASTM D785
|
|
M 级
|
92
|
|
|
|
R 级
|
127
|
|
|
|
抗张强度 2
|
|
|
ASTM D638
|
|
屈服
|
65.5
|
MPa
|
|
|
断裂
|
77.9
|
MPa
|
|
|
伸长率 2 (断裂)
|
78
|
%
|
ASTM D638
|
|
弯曲模量 3 (50.0 mm 跨距)
|
2330
|
MPa
|
ASTM D790
|
|
弯曲强度 3 (屈服, 50.0 mm 跨距)
|
97.2
|
MPa
|
ASTM D790
|
|
悬壁梁缺口冲击强度 (23°C)
|
370
|
J/m
|
ASTM D256
|
|
无缺口悬臂梁冲击 (23°C)
|
3200
|
J/m
|
ASTM D4812
|
|
落锤冲击 (23°C)
|
149
|
J
|
ASTM D3029
|
|
拉伸冲击强度 4
|
578
|
kJ/m²
|
ASTM D1822
|
|
载荷下热变形温度 (1.8 MPa, 未退火, 3.20 mm)
|
149
|
°C
|
ASTM D648
|
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
8.1E-5
|
cm/cm/°C
|
ASTM E831
|
|
比热
|
1260
|
J/kg/°C
|
ASTM C351
|
|
导热系数
|
0.21
|
W/m/K
|
ASTM C177
|
|
RTI Elec
|
130
|
°C
|
UL 746
|
|
RTI Imp
|
130
|
°C
|
UL 746
|
|
RTI
|
130
|
°C
|
UL 746
|
|
体积电阻率
|
> 2.5E+17
|
ohms·cm
|
ASTM D257
|
|
介电强度 (3.20 mm, in Air)
|
20
|
kV/mm
|
ASTM D149
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
3.27
|
|
|
|
60 Hz
|
3.27
|
|
|
|
1 MHz
|
3.10
|
|
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
1.6E-3
|
|
|
|
60 Hz
|
1.6E-3
|
|
|
|
100 Hz
|
0.026
|
|
|
|
耐电弧性 5
|
PLC 6
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 3
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746
|
|
折射率
|
1.600
|
|
ASTM D542
|
|
透射率 (2540 µm)
|
85.0
|
%
|
ASTM D1003
|
|
雾度 (2540 µm)
|
1.0
|
%
|
ASTM D1003
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
327 到 349
|
°C
|
|
|
料筒中部温度
|
338 到 360
|
°C
|
|
|
料筒前部温度
|
349 到 371
|
°C
|
|
|
射嘴温度
|
343 到 366
|
°C
|
|
|
加工（熔体）温度
|
349 到 371
|
°C
|
|
|
模具温度
|
82.2 到 116
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
|
|