比重
|
1.19
|
|
ASTM D792
|
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
14
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动 (0.126 in)
|
6.0E-3 到 8.0E-3
|
in/in
|
内部方法
|
|
室外适用性
|
f1
|
|
UL 746C
|
|
拉伸模量 3
|
329000
|
psi
|
ASTM D638
|
|
抗张强度 4
|
|
|
ASTM D638
|
|
屈服
|
8990
|
psi
|
|
|
断裂
|
9430
|
psi
|
|
|
伸长率 4
|
|
|
ASTM D638
|
|
屈服
|
6.0
|
%
|
|
|
断裂
|
130
|
%
|
|
|
弯曲模量 5 (1.97 in 跨距)
|
339000
|
psi
|
ASTM D790
|
|
弯曲强度 5 (屈服, 1.97 in 跨距)
|
14600
|
psi
|
ASTM D790
|
|
悬壁梁缺口冲击强度 (73°F)
|
15
|
ft·lb/in
|
ASTM D256
|
|
装有测量仪表的落镖冲击 (73°F, Total Energy)
|
646
|
in·lb
|
ASTM D3763
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.126 in
|
279
|
°F
|
|
|
264 psi, 未退火, 0.126 in
|
259
|
°F
|
|
|
维卡软化温度
|
289
|
°F
|
ASTM D1525 6
|
|
线形热膨胀系数
|
|
|
ASTM E831
|
|
流动 : -40 到 104°F
|
3.7E-5
|
in/in/°F
|
|
|
横向 : -40 到 104°F
|
3.7E-5
|
in/in/°F
|
|
|
RTI Elec
|
266
|
°F
|
UL 746
|
|
RTI Imp
|
248
|
°F
|
UL 746
|
|
RTI
|
266
|
°F
|
UL 746
|
|
耐电弧性 7
|
PLC 7
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 2
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746
|
|
UL 阻燃等级 (0.0598 in)
|
V-0
|
|
UL 94
|
|
灼热丝易燃指数 (0.0394 in)
|
1760
|
°F
|
IEC 60695-2-12
|
|
热灯丝点火温度 (0.0394 in)
|
1610
|
°F
|
IEC 60695-2-13
|
|
干燥温度
|
250
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
510 到 550
|
°F
|
|
|
料筒中部温度
|
530 到 570
|
°F
|
|
|
料筒前部温度
|
550 到 590
|
°F
|
|
|
射嘴温度
|
540 到 580
|
°F
|
|
|
加工（熔体）温度
|
550 到 590
|
°F
|
|
|
模具温度
|
160 到 200
|
°F
|
|
|
背压
|
50.0 到 100
|
psi
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
1.0E-3 到 3.0E-3
|
in
|
|
|