比重
|
|
|
|
|
--
|
1.18
|
|
ASTM D792
|
|
--
|
1.19
|
g/cm³
|
ISO 1183
|
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
10
|
g/10 min
|
ASTM D1238
|
|
溶化体积流率（MVR） (300°C/1.2 kg)
|
0.549
|
in³/10min
|
ISO 1133
|
|
收缩率
|
|
|
内部方法
|
|
流动 : 0.126 in
|
4.0E-3 到 8.0E-3
|
in/in
|
|
|
横向流动 : 0.126 in
|
4.0E-3 到 8.0E-3
|
in/in
|
|
|
吸水率
|
|
|
ISO 62
|
|
饱和, 73°F
|
0.35
|
%
|
|
|
平衡, 73°F, 50% RH
|
0.15
|
%
|
|
|
拉伸模量
|
|
|
|
|
-- 3
|
305000
|
psi
|
ASTM D638
|
|
--
|
305000
|
psi
|
ISO 527-2/1
|
|
抗张强度
|
|
|
|
|
屈服 4
|
8410
|
psi
|
ASTM D638
|
|
屈服
|
7980
|
psi
|
ISO 527-2/50
|
|
断裂 4
|
8700
|
psi
|
ASTM D638
|
|
断裂
|
8700
|
psi
|
ISO 527-2/50
|
|
伸长率
|
|
|
|
|
屈服 4
|
6.0
|
%
|
ASTM D638
|
|
屈服
|
6.0
|
%
|
ISO 527-2/50
|
|
断裂 4
|
130
|
%
|
ASTM D638
|
|
断裂
|
130
|
%
|
ISO 527-2/50
|
|
弯曲模量
|
|
|
|
|
1.97 in 跨距 5
|
299000
|
psi
|
ASTM D790
|
|
-- 6
|
319000
|
psi
|
ISO 178
|
|
弯曲应力
|
|
|
|
|
-- 6, 7
|
12300
|
psi
|
ISO 178
|
|
屈服, 1.97 in 跨距 5
|
12900
|
psi
|
ASTM D790
|
|
简支梁缺口冲击强度 8
|
|
|
ISO 179/1eA
|
|
-22°F
|
29
|
ft·lb/in²
|
|
|
73°F
|
36
|
ft·lb/in²
|
|
|
简支梁无缺口冲击强度 8
|
|
|
ISO 179/1eU
|
|
-22°F
|
无断裂
|
|
|
|
73°F
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
-22°F
|
12
|
ft·lb/in
|
ASTM D256
|
|
73°F
|
15
|
ft·lb/in
|
ASTM D256
|
|
-22°F 9
|
24
|
ft·lb/in²
|
ISO 180/1A
|
|
73°F 9
|
33
|
ft·lb/in²
|
ISO 180/1A
|
|
无缺口伊佐德冲击强度 9
|
|
|
ISO 180/1U
|
|
-22°F
|
无断裂
|
|
|
|
73°F
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击 (73°F, Total Energy)
|
443
|
in·lb
|
ASTM D3763
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.126 in
|
275
|
°F
|
|
|
264 psi, 未退火, 0.126 in
|
248
|
°F
|
|
|
维卡软化温度
|
284
|
°F
|
ISO 306/B120, ASTM D1525 10
|
|
Ball Pressure Test (257°F)
|
Pass
|
|
IEC 60695-10-2
|
|
线形热膨胀系数
|
|
|
|
|
流动 : -40 到 104°F
|
3.6E-5
|
in/in/°F
|
ASTM E831
|
|
流动 : 73 到 176°F
|
4.0E-5
|
in/in/°F
|
ISO 11359-2
|
|
横向 : -40 到 104°F
|
3.6E-5
|
in/in/°F
|
ASTM E831
|
|
横向 : 73 到 176°F
|
4.3E-5
|
in/in/°F
|
ISO 11359-2
|
|
RTI Elec
|
257
|
°F
|
UL 746
|
|
RTI Imp
|
239
|
°F
|
UL 746
|
|
RTI
|
248
|
°F
|
UL 746
|
|
介电强度
|
|
|
|
|
0.126 in, in Oil
|
430
|
V/mil
|
ASTM D149
|
|
0.126 in, 在油中
|
410
|
V/mil
|
IEC 60243-1
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
2.95
|
|
|
|
60 Hz
|
2.95
|
|
|
|
1 MHz
|
2.90
|
|
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
2.4E-3
|
|
|
|
60 Hz
|
2.4E-3
|
|
|
|
1 MHz
|
8.5E-3
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746
|
|
漏电起痕指数
|
225
|
V
|
IEC 60112
|
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
0.0591 in
|
V-0
|
|
|
|
0.118 in
|
5VA
|
|
|
|
灼热丝易燃指数 (0.0394 in)
|
1760
|
°F
|
IEC 60695-2-12
|
|
热灯丝点火温度 (0.0394 in)
|
1520
|
°F
|
IEC 60695-2-13
|
|
干燥温度
|
250
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
423 到 559
|
°F
|
|
|
料筒中部温度
|
540 到 579
|
°F
|
|
|
料筒前部温度
|
559 到 601
|
°F
|
|
|
射嘴温度
|
550 到 590
|
°F
|
|
|
加工（熔体）温度
|
559 到 601
|
°F
|
|
|
模具温度
|
160 到 199
|
°F
|
|
|
背压
|
50.0 到 100
|
psi
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
1.0E-3 到 3.0E-3
|
in
|
|
|