比重
|
1.30
|
|
ASTM D792
|
|
收缩率
|
|
|
内部方法
|
|
流动 : 0.126 in
|
8.0E-3 到 0.010
|
in/in
|
|
|
横向流动 : 0.126 in
|
8.0E-3 到 0.010
|
in/in
|
|
|
室外适用性
|
f2
|
|
UL 746C
|
|
抗张强度 3
|
|
|
ASTM D638
|
|
屈服
|
6800
|
psi
|
|
|
断裂
|
5800
|
psi
|
|
|
伸长率 3
|
|
|
ASTM D638
|
|
屈服
|
5.0
|
%
|
|
|
断裂
|
70
|
%
|
|
|
弯曲模量 4 (1.97 in 跨距)
|
270000
|
psi
|
ASTM D790
|
|
弯曲强度 4 (屈服, 1.97 in 跨距)
|
9700
|
psi
|
ASTM D790
|
|
悬壁梁缺口冲击强度
|
|
|
ASTM D256
|
|
-40°F
|
8.0
|
ft·lb/in
|
|
|
-4°F
|
13
|
ft·lb/in
|
|
|
73°F
|
14
|
ft·lb/in
|
|
|
装有测量仪表的落镖冲击
|
|
|
ASTM D3763
|
|
-40°F, Total Energy
|
420
|
in·lb
|
|
|
-4°F, Total Energy
|
396
|
in·lb
|
|
|
73°F, Total Energy
|
400
|
in·lb
|
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.126 in
|
218
|
°F
|
|
|
264 psi, 未退火, 0.126 in
|
155
|
°F
|
|
|
维卡软化温度
|
|
|
|
|
--
|
239
|
°F
|
ASTM D1525 5
|
|
--
|
252
|
°F
|
ISO 306/B120
|
|
线形热膨胀系数
|
|
|
|
|
流动 : -40 到 104°F
|
5.3E-5
|
in/in/°F
|
ASTM E831, ISO 11359-2
|
|
横向 : -40 到 104°F
|
5.4E-5
|
in/in/°F
|
ASTM E831
|
|
横向 : -40 到 104°F
|
5.6E-5
|
in/in/°F
|
ISO 11359-2
|
|
RTI Elec
|
167
|
°F
|
UL 746
|
|
RTI Imp
|
167
|
°F
|
UL 746
|
|
RTI
|
167
|
°F
|
UL 746
|
|
耐电弧性 6
|
PLC 5
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 0
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
0.0580 in
|
V-0
|
|
|
|
0.118 in
|
5VA
|
|
|
|
极限氧指数
|
28
|
%
|
ASTM D2863
|
|
干燥温度
|
250
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
12
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
460 到 490
|
°F
|
|
|
料筒中部温度
|
470 到 500
|
°F
|
|
|
料筒前部温度
|
480 到 510
|
°F
|
|
|
射嘴温度
|
470 到 500
|
°F
|
|
|
加工（熔体）温度
|
480 到 510
|
°F
|
|
|
模具温度
|
120 到 170
|
°F
|
|
|
背压
|
50.0 到 100
|
psi
|
|
|
螺杆转速
|
50 到 100
|
rpm
|
|
|
排气孔深度
|
1.0E-3 到 1.5E-3
|
in
|
|
|